Home >> Products Specification >> (Delrin® 900P NC010)
Delrin® 900P NC010
 
Description
Delrin® 900P NC010 is a low viscosity acetal homopolymer resin for multicavity and thin wall molding. It offers an improved processing thermal stability.
 
Physical Properties
Properties Test
Method
Unit Value
Identification      
Resin Identification ISO 1043   POM
Part Marking Code ISO 11469   >POM<
Mechanical      
Yield Stress ISO 527 MPa (kpsi) 71 (10.3)
Yield Strain ISO 527 % 13
Strain at Break
50mm/min
ISO 527 %
28
Nominal Strain at Break ISO 527 % 23
Tensile Modulus ISO 527 MPa (kpsi) 3300 (479)
Tensile Creep Modulus
1h
1000h
ISO 899 MPa (kpsi)
2800 (406)
1500 (218)
Flexural Modulus ISO 178 MPa (kpsi) 3000 (435)
Notched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
ISO 179/1eA kJ/m2
7
8
Unnotched Charpy Impact Strength
-30°C (-22°F)
23°C (73°F)
ISO 179/1eU kJ/m2
200
200
Thermal      
Deflection Temperature
0.45MPa
1.80MPa
ISO 75-1/-2 °C (°F)
162 (324)
94 (201)
Melting Temperature
10°C/min
ISO 11357-1/-3 °C (°F)
178 (352)
CLTE, Normal
23 - 55°C (73 - 130°F)
ISO 11359-1/-2 E-4/C (E-4/F)
1.2 (0.67)
CLTE, Parallel
23 - 55°C (73 - 130°F)
ISO 11359-1/-2 E-4/C (E-4/F)
1.2 (0.67)
Vicat Softening Temperature
50N
ISO 306 °C (°F)
160 (320)
Rheological      
Melt Mass-Flow Rate
190°C, 2.16kg
ISO 1133 g/10 min
2.5
Electrical      
Surface Resistivity IEC 60093 ohm >1E15
Volume Resistivity IEC 60093 ohm m 1E12
Electric Strength
1.0mm
IEC 60243-1 kV/mm (V/mil)
32 (812)
Relative Permittivity
1E2 Hz
1E6 Hz
IEC 60250  
3.8
3.8
Dissipation Factor
1E2 Hz
1E6 Hz
IEC 60250 E-4
180
50
CTI IEC 60112 V 600
Flammability      
Flammability Classification
0.75mm
IEC 60695-11-10  
HB
Flammability Classification
0.75mm
UL94  
HB
Oxygen Index ISO 4589-1/-2 % 23
High Amperage Arc Ignition Resistance
0.75mm
UL 746A arcs
200
Hot Wire Ignition
0.75mm
1.5mm
3.0mm
UL 746A s
8
13
22
Temperature Index      
RTI, Electrical
0.75mm
1.5mm
3.0mm
UL 746B °C
50
110
110
RTI, Impact
0.75mm
1.5mm
3.0mm
UL 746B °C
50
85
90
RTI, Strength
0.75mm
1.5mm
3.0mm
UL 746B °C
50
90
95
Other      
Density ISO 1183 kg/m3(g/cm3) 1420 (1.42)
Hardness, Rockwell
Scale M
Scale R
ISO 2039/2  
92
120
Water Absorption
Equilibrium 50%RH
Immersion 24h
Saturation, immersed
ISO 62, Similar to %
0.26
0.56
1.40
Molding Shrinkage
Normal, 2.0mm
Parallel, 2.0mm
ISO 294-4 %
1.9
1.9
Processing      
Melt Temperature Range   °C (°F) 210-220 (410-430)
Melt Temperature Optimum   °C (°F) 215 (420)
Mold Temperature Range   °C (°F) 80-100 (175-210)
Mold Temperature Optimum   °C (°F) 90 (195)
Drying Time, Dehumidified Dryer   h 2-4
Drying Temperature   °C (°F) 80 (175)
Processing Moisture Content   % <0.2
Hold Pressure Range   MPa (kpsi) 80-100 (12-15)